Kwik Mix 5 kg. Build and Restore Concrete Patch
KWIK MIX 11 lb. Grey Build and Restore Concrete Patch is a high strength, rapid developing, commercial grade concrete patch containing 2 Portland Cements, silica fume, active silicates, special aggregate, a super plasticizer, defoamer and a set-accelerator. The patch will form a very dense patch that will resist chlorides and acids. Specifically designed for remedial patching ,repairing and restoration of worn or damaged concrete structures and surfaces. Suggested uses are curbs, roads, sidewalks, bridges, pools, decks, foundations, ornamental casts and other building applications. For best results, after the initial set has taken place the surface may be moistened and troweled to a smooth finish. For maximum strength, cure the surface (keep damp) for a 24 hour period. For deep depressions, the patch should be placed in maximum 2 inch deep layers.
Features
- Very low chloride permeability
- High salt resistance
- Very high freeze-thaw resistance
- High compressive and shear/bond strengths
Specifications
| Initial Set Time | 30 minutes (ASTM C807) |
| Compressive Strength | 2 hours 1080 psi (ASTM C579B) |
| Compressive Strength | 28 days 7640 psi (ASTM C579B) |
| Shear/Bond | 28 days 1566 psi (ASTM C882) |
| Chloride Permeability | 14 days 1498 coul (ASTM C1202) |
| Dry Shrinkage | 28 days 0.0907% (ASTM C596) |
Original: $14.50
-65%$14.50
$5.07Kwik Mix 5 kg. Build and Restore Concrete Patch
KWIK MIX 11 lb. Grey Build and Restore Concrete Patch is a high strength, rapid developing, commercial grade concrete patch containing 2 Portland Cements, silica fume, active silicates, special aggregate, a super plasticizer, defoamer and a set-accelerator. The patch will form a very dense patch that will resist chlorides and acids. Specifically designed for remedial patching ,repairing and restoration of worn or damaged concrete structures and surfaces. Suggested uses are curbs, roads, sidewalks, bridges, pools, decks, foundations, ornamental casts and other building applications. For best results, after the initial set has taken place the surface may be moistened and troweled to a smooth finish. For maximum strength, cure the surface (keep damp) for a 24 hour period. For deep depressions, the patch should be placed in maximum 2 inch deep layers.
Features
- Very low chloride permeability
- High salt resistance
- Very high freeze-thaw resistance
- High compressive and shear/bond strengths
Specifications
| Initial Set Time | 30 minutes (ASTM C807) |
| Compressive Strength | 2 hours 1080 psi (ASTM C579B) |
| Compressive Strength | 28 days 7640 psi (ASTM C579B) |
| Shear/Bond | 28 days 1566 psi (ASTM C882) |
| Chloride Permeability | 14 days 1498 coul (ASTM C1202) |
| Dry Shrinkage | 28 days 0.0907% (ASTM C596) |
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
KWIK MIX 11 lb. Grey Build and Restore Concrete Patch is a high strength, rapid developing, commercial grade concrete patch containing 2 Portland Cements, silica fume, active silicates, special aggregate, a super plasticizer, defoamer and a set-accelerator. The patch will form a very dense patch that will resist chlorides and acids. Specifically designed for remedial patching ,repairing and restoration of worn or damaged concrete structures and surfaces. Suggested uses are curbs, roads, sidewalks, bridges, pools, decks, foundations, ornamental casts and other building applications. For best results, after the initial set has taken place the surface may be moistened and troweled to a smooth finish. For maximum strength, cure the surface (keep damp) for a 24 hour period. For deep depressions, the patch should be placed in maximum 2 inch deep layers.
Features
- Very low chloride permeability
- High salt resistance
- Very high freeze-thaw resistance
- High compressive and shear/bond strengths
Specifications
| Initial Set Time | 30 minutes (ASTM C807) |
| Compressive Strength | 2 hours 1080 psi (ASTM C579B) |
| Compressive Strength | 28 days 7640 psi (ASTM C579B) |
| Shear/Bond | 28 days 1566 psi (ASTM C882) |
| Chloride Permeability | 14 days 1498 coul (ASTM C1202) |
| Dry Shrinkage | 28 days 0.0907% (ASTM C596) |